Hard Alloy Adhesive Ethyl Cellulose,
Industrial Grade Ethyl Cellulose,
25kg bag Ethyl Cellulose Polymer
Ethyl Cellulose K70 K100 for adhesive in hard alloy
The cemented carbide sintering process can be divided into four basic stages:
1. Removal of forming agent and pre-sintering stage, at this stage the sintered body undergoes the following changes:
Removal of the forming agent, as the temperature rises in the initial stage of sintering, the forming agent gradually decomposes or vaporizes to remove the sintered body. At the same time, the forming agent more or less carbonizes the sintered body, and the amount of carbon increase will follow the forming agent The type, quantity, and sintering process vary.
The oxides on the powder surface are reduced. At the sintering temperature, hydrogen can reduce the oxides of cobalt and tungsten. If the forming agent is removed in vacuum and sintering, the carbon-oxygen reaction is not strong. The contact stress between the powder particles is gradually eliminated, the bonding metal powder begins to recover and recrystallize, surface diffusion begins to occur, and the strength of the compact increases.
2. Solid phase sintering stage (800℃--eutectic temperature)
At the temperature before the appearance of the liquid phase, in addition to continuing the process that occurred in the previous stage, the solid phase reaction and diffusion are intensified, the plastic flow is enhanced, and the sintered body shrinks significantly.
3. Liquid phase sintering stage (eutectic temperature-sintering temperature)
When the sintered body appears in the liquid phase, the shrinkage is quickly completed, and then crystalline transformation occurs, forming the basic structure and structure of the alloy.
4. Cooling stage (sintering temperature-room temperature)
At this stage, the structure and phase composition of the alloy change with different cooling conditions. This feature can be used to heat the cemented carbide to improve its physical and mechanical properties.
Name: Ethyl Cellulose
In the formula , n stands for degree of polymerization and R for –H or –C2H5 .
Ethyl Cellulose is a kind of white grains or powder, having no smell or tastes . Its 5% soliquoid shows neutral to litmus test paper . Its specific density 1 . 07~1 . 18 , heat distortion point: 135~155degree centigrade , and fire point: 330~360 degree centigrade . Ethyl Cellulose has good stability to light , heat , oxygen and wetness , and is stable to chemicals . It is resistant to alcali , dilute acid and salting liquid , soluble in some organic solvents , such as alcohol , ether, ketone , ester, aromatic hydrocarbon and halohydrocarbon , etc , and compatible to many celluloses , resin and nearly all plasticizers . Ethyl Cellulose has low combustibility, small hydroscopicity and good electric behavior . Its thin film and plastics have good mechanical strength and flexibility in a wide range of temperature .
1. Appearance: White or even yellowing powder or grains , having no smell or taste .
2. Technical Index
|K type||N type||T type|
|Content of ethoxy, %||45 . 0~47 . 9||48 . 0~49 . 5||49 . 6 Min|
|Viscosity, mPas||Conform to the requirements of table 2|
|Ash , %||0 .4 Max|
|Moisture , %||3 . 0 Max|
3 .Viscosity Specification
|Level||Specific range||Level||Specific range|
|6||5 0～8 0||70||62～74|
|10||8 . 1～12||90||80~90|
|55||51～60||300||250 Min .|
Ethyl Cellulose is widely used in paints for various products , such as wooden products (furniture) , metal surfaces , paper, rubber, thermotropic products and integrated circuits; in ink such as screen printing ink , magnetic ink , intaglio and amine printing ink; as freezing-resistant material and all kinds of precise membrane module used in aviation industry; as the special plastics and precipitate such as rocket propellant coating band; as electrical insulation and cable coating; as high molecular suspension polymerizing and dispersing agent; as adhensive in hard alloy and ceramics; and used as dye printing slurry in textile industry .
It is packed in paper bags lined with PVC bags . Net weight per package: 20kg